Effect of different application strategies of universal adhesive used for immediate and delayed dentin sealing on the microtensile bond strength of self-adhesive resin cement to dentin with and without aging.

抄録

背景:

間接修復物の接着強度は、特に注意を払うべき非常に重要な課題である。近年，即時象牙質封鎖（IDS）法が提案されている．本研究の目的は，即時象牙質封鎖法と遅延象牙質封鎖法（DDS）のためのユニバーサル接着剤塗布の異なる戦略が，自己接着性レジンセメントの微小引張接着強さ（μTBS）に及ぼす影響を，経時変化の有無により検討することであった．

BACKGROUND: Bond strength of indirect restorations is a very important issue that should be given special attention. Immediate dentin sealing (IDS) technique has been suggested in recent years. The aim of the present study was to investigate the effect of different strategies of universal adhesive application for immediate and delayed dentin sealing (DDS) on the microtensile bond strength (μTBS) of self-adhesive resin cement with and without aging.

材料および方法:

本実験では、健康なヒトの第三大臼歯24本を選択した。咬合象牙質を露出させた後、オールボンドユニバーサル接着剤の塗布方法（エッチアンドリンスまたはセルフエッチ）に基づき、ランダムに2つのグループ（12人）に分けられた。各群はさらに、IDS法またはDDS法に基づいて2群（n=6）に細分化された。その後、コンポジットブロックを自己接着性レジンセメントで咬合面上に固着した。試料を1 mm2断面に切断した後，各サブグループの試料の半分を1週間後にμTBS試験に供し，残りの半分を10,000熱サイクル後にμTBS試験に供した．データは三元配置のANOVAを用いて分析した（<0.05）。

MATERIAL AND METHODS: In this experimental study, 24 healthy human third molars were selected. After exposing the occlusal dentin, the teeth were randomly divided into two groups of 12 based on the All-Bond Universal adhesive application strategy (etch-and-rinse or self-etch). Each group was further subdivided into two (n=6) based on IDS or DDS technique. Then composite blocks were cemented on the occlusal surface with self-adhesive resin cement. After cutting the samples into 1 mm2 cross-sections, half of the samples of each subgroup were subjected to µTBS test after one week, and the other half were tested under μTBS after 10,000 thermal cycles. Data were analyzed using three-way ANOVA (<0.05).

結果:

μTBSは，ボンドストラテジー，シーリングテクニック，エージングの3因子すべてに有意に影響された。また，3因子間には有意な相互作用が認められた．

RESULTS: μTBS was significantly affected by all three factors of bond strategy, sealing technique and aging. There was also a significant interaction between the three factors.

結論:

即時象牙質シーリングはμTBSを改善した。エッチング＆リンス法はμTBSが高くなり，加齢はμTBSの低下を招いた．接着剤，デンタルボンディング，象牙質，ユニバーサル，シーリング．

CONCLUSIONS: Immediate dentin sealing improved μTBS. The etch-and-rinse strategy resulted in higher μTBS, while aging led to a decrease in μTBS. Adhesives, dental bonding, dentin, universal, sealing.