新規に製造した減感作剤、クロルヘキシジンおよびグルマのコンポジットと象牙質との接着強度および接着寿命に対するin vitro比較評価

In Vitro Comparative Evaluation of Newly Produced Desensitizer, Chlorhexidine and Gluma on Bond Strength and Bond Longevity of Composite to Dentin.

• Reza Davalloo
• Seyedeh Maryam Tavangar
• Heshmatollah Ebrahimi
• Farideh Darabi
• Shima Mahmoudi

抄録

問題点の説明:

象牙質のエッチング処理は，脱灰した象牙質の有機マトリックスを加水分解するマトリックスメタロプロテアーゼ（MMP）を活性化させることができる．グルマとクロルヘキシジンはMMPの活性化を抑制した．

Statement of the Problem:  Etching process on dentin can activate matrix metalloproteinase (MMP) which hydrolyze organic matrix of demineralized dentin. Gluma and chlorhexidine could inhibit the activation of MMP.

目的:

本研究の目的は，グルマとクロルヘキシジンを併用した新しい脱感作材料が複合修復物のせん断接着強さと接着耐久性に及ぼす影響を評価することであった．

Purpose:  The aim of the study was to evaluate the effect of a new desensitizing material consisting of Gluma and chlorhexidine together on the shear bond strength and bond durability of composite restorations.

材料と方法:

齲蝕のない前歯を抜歯した100名20名の前歯を冠冠冠の3分の1から水平に切除し、平坦な象牙質表面を露出させ、無作為に4群に分けた。対照群では、表面処理は行わなかった。第1群ではクロルヘキシジン（CHX）2％、第2群では新材料（NM）、第3群ではグルマ脱感作剤（GD）をエッチング後、接着前に塗布した（トータルエッチング接着システム）。接合後、円筒状の金型を用いて試料の表面に複合体を配置した。その後、２４時間後に半分の試験片を、残りの半分の試験片を蒸留水中で６ヶ月間保存し、熱サイクルを行った後のせん断接着強さを測定した。試験片の破壊形態は実体顕微鏡を用いて評価した。データはSPSSソフトウェアの一方向アノバ検定およびTukey's Post Hoc検定を用いて解析した．

Materials and Method: One hundred and twenty caries-free extracted premolars were sectioned horizontally from one third of the coronal crown to expose flat dentin surface and randomly divided into 4 groups. In the control group, no surface treatment was used. In the first group chlorhexidine (CHX) 2%, in the second group, new material (NM) and in third group Gluma desensitizer (GD) was applied after etching and before bonding(total-etch bonding system). After the bonding process, the composite was placed on the surface of the samples using a cylindrical mold. Then, the shear bond strengths of half of the specimens were measured after 24 hours and the other half after 6 months of storage in distilled water and thermocycling. The failure types of specimens were evaluated with a stereomicroscope. Data were analyzed using One-way Anova and Tukey's Post Hoc tests in SPSS software.

結果:

また，6ヶ月後のせん断接着強さが最も高いのはNM群とGD群であり，統計的に有意な差は認められなかった。24時間接着強さは群間で有意な差は認められなかった。混合破壊の発生率は全群で最も高かった。

Results:   After 6 months, the bond strength decreased in all groups and differences were statistically significant (= 0.002).The highest shear bond strength was observed after 6 months in the NM group and the GD group with no statistically significant difference. The 24-hour bond strengths were not significant between groups. Mix failure had the highest rate in all groups.

結論:

クロルヘキシジンとグルマの併用による経時的な結合の完全性と強度の維持効果は、グルマ化合物単独の場合と同様であり、クロルヘキシジンよりも優れた効果があると結論づけることができます。

Conclusion:  It can be concluded that the effect of combination of chlorhexidine and Gluma on maintaining the integrity and strength of bond over time is similar to Gluma compound alone and they have better effect than chlorhexidine.