異なる灌漑用水と接触したケイ酸カルシウム系材料の着色安定性

Color stabilities of calcium silicate-based materials in contact with different irrigation solutions.

抄録

はじめに:

三酸化無機骨材（MTA）は，審美領域に適用した場合，歯牙の変色を引き起こすことが報告されている．これまでの研究で，根管治療液と接触した際のMTAの変色が報告されている．さらに，新規のケイ酸カルシウム系材料の色安定性に関するデータは限られている．本研究では、4種類のケイ酸カルシウム系材料について、異なる根管治療液との接触による色の変化を評価することを目的とした。

INTRODUCTION: Mineral trioxide aggregate (MTA) has been reported to cause tooth discoloration when applied in the esthetic zone. A previous study has shown discoloration of MTA in contact with root canal irrigation solutions. Moreover, there are limited data on color stability of novel calcium silicate-based materials. This study aimed to evaluate color changes of 4 calcium silicate-based materials in contact with different irrigation solutions.

方法:

ProRoot white MTA（Dentsply Tulsa Dental, Johnson City, TN），ホワイトMTA Angelus（Angelus Solucoes Odontologicas, Londrina, Brazil），Biodentine（Septodont, Saint Maur des Fosses, France），およびBioAggregate（ Innovative Bioceramix, Vancouver, BC, Canada）試料を評価した．材料は、製造業者の説明書に従って混合した。湿度100%，37℃で各材料の設定時間だけ型に入れて硬化させ，円柱状のサンプル（直径10mm，高さ2mm）を得た．各試料を5%次亜塩素酸ナトリウム，2%グルコン酸クロルヘキシジン，または蒸留水中に24時間浸漬した．色調の変化は分光光度計で測定した．データは2元配置分散分析およびBonferroni検定により解析した。

METHODS: ProRoot white MTA (Dentsply Tulsa Dental, Johnson City, TN), white MTA Angelus (Angelus Solucoes Odontologicas, Londrina, Brazil), Biodentine (Septodont, Saint Maur des Fosses, France), and BioAggregate (Innovative Bioceramix, Vancouver, BC, Canada) samples were assessed. Materials were mixed according to the manufacturers' instructions. Cylindric samples (10-mm diameter and 2-mm height) were obtained by curing in molds for each material's setting time at 100% humidity and 37°C. Each specimen was immersed in 5% sodium hypochlorite, 2% chlorhexidine gluconate, or distilled water for 24 hours. Color changes were measured with a spectrophotometer. Data were analyzed by using 2-way analysis of variance and post hoc Bonferroni tests.

結果:

次亜塩素酸ナトリウムおよびグルコン酸クロルヘキシジンに浸漬すると，すべての材料が臨床的に知覚可能な変色を示した．プロルート白色MTAは、Bioaggregate、Biodentine、白色MTA Angelusと統計的に有意な差を示した。また，蒸留水は，どの材料においても臨床的に認 められる変色を生じさせなかった．

RESULTS: All materials exhibited clinically perceptible discoloration when immersed in sodium hypochlorite and chlorhexidine gluconate. ProRoot white MTA showed a statistically significant difference from Bioaggregate, Biodentine, and white MTA Angelus. Distilled water did not cause clinically perceptible discoloration of any material.

結論:

審美的に重要な部位では、酸化ビスマスを含まないコンパウンド、バイオデンティン、バイオアグレゲートをMTAの代替品として検討することが可能である。しかし、すべてのケイ酸カルシウム系材料は、臨床的に知覚可能な色調変化を示した。

CONCLUSIONS: In esthetically critical regions, compounds free of bismuth oxide, Biodentine, and BioAggregate can be considered as alternatives to MTA. However, all calcium silicate-based materials exhibited clinically perceptible color changes.