銅-ニッケル-チタン製歯列矯正用アーチワイヤーの機械的特性および表面性状に及ぼすフラワー化ナトリウム洗口液およびココナッツオイルによるオゾン注入オイルプリング液の影響

Effect of Sodium Flouride Mouthwash and Ozone-Infused Oil Pulling Solution With Coconut Oil on Mechanical Properties and Surface Characterization of Copper-Nickel-Titanium Orthodontic Archwires.

抄録

目的と目標:

0.016 "のプレハブ銅-ニッケル-チタン（Cu-Ni-Ti）タイプ35C（Ormco Company, USA）アーチワイヤーに、0.05%のフッ化ナトリウム（NaF）洗口液（ACT Anti-Cavity Fluoride Mouthwash, Sanofi Company, USA）およびココナッツオイル（O）（O Essentials, Health Ranger Store, USA）を添加したオゾン入りオイルプリング溶液をかけたときの機械的特性と表面特性への影響を調べること。

AIMS AND OBJECTIVES: To determine the impact on the mechanical properties and surface characteristics of prefabricated 0.016" copper-nickel-titanium (Cu-Ni-Ti) type 35C (Ormco Company, USA) archwires when subjected to 0.05% sodium fluoride (NaF) mouthwash (ACT Anti-Cavity Fluoride Mouthwash, Sanofi Company, USA) and ozone-infused oil-pulling solution with coconut oil (O) (O Essentials, Health Ranger Store, USA).

材料と方法:

上顎0.016 "Cu-Ni-Tiアーチワイヤーを60サンプル、長さ25mmになるように後端ストレート部で切断し、3つのグループ（n=20）に均等に分配した。各群のワイヤーを蒸留水（dHO）、NaF、O溶液に37℃で90分間浸漬した。すべてのサンプルを溶液から取り出し、試験前に蒸留水で洗浄した。万能試験機を用いて、15個のサンプルについて3点曲げ試験を行った。降伏強度（YS）、曲げ弾性率（E）、スプリングバック比（YS/E）を算出した。それぞれの溶液から得られた残りの5つのサンプルは、表面形状評価のために走査型電子顕微鏡（SEM）で観察された。

MATERIALS AND METHODS: Sixty samples of preformed maxillary 0.016" Cu-Ni-Ti archwires were cut at the straight posterior ends for a length of 25 mm and then equally distributed into three groups (n=20). Each group of wires was immersed in distilled water (dHO), NaF, and O solutions for 90 minutes at 37C. All samples were taken out of their solutions and washed with distilled water prior to testing. On a universal testing device, a three-point bending test was performed on 15 samples. Yield strength (YS), flexural modulus of elasticity (E), and springback ratio (YS/E) were calculated. The remaining five samples from respective solutions were observed under a scanning electron microscope (SEM) for surface topography evaluation.

結果:

NaFとOの負荷YS、E、YS/Eの平均差はそれぞれ41.14MPa、4.58GPa、-0.0006であったのに対し、無負荷の値はそれぞれ23.45MPa、4.38GPa、-0.0004であり、統計的有意性は<0.001であった。表面トポグラフィーの変化は、O溶液と比較してNaF洗口群で認められた。

RESULTS: The mean differences in loading YS, E, and YS/E between NaF and O are 41.14 MPa, 4.58 GPa, and -0.0006 whereas unloading values are 23.45 MPa, 4.38 GPa, and -0.0004, respectively with a statistical significance of <0.001. Surface topography alteration was appreciated in the NaF mouthwash group compared to the O solution.

結論:

0.016 "Cu-Ni-Tiアーチワイヤーの荷重負荷時および負荷解除時の機械的特性は、NaF洗口液およびO溶液に暴露した後に変化した。Cu-Ni-Tiアーチワイヤーの機械的特性は、O溶液よりもNaF洗口液によりマイナスの影響を受けた。フッ化ナトリウム洗口液は、O液と比較してより腐食性の変化が大きい。

CONCLUSIONS: The mechanical properties of 0.016" Cu-Ni-Ti archwires during loading and unloading were changed after exposure to NaF mouthwash and O solution. The mechanical properties of Cu-Ni-Ti archwires were more negatively affected by NaF mouthwash than by O solution. Sodium fluoride mouthwash offers more corrosive changes when compared with the O solution.